結晶系
ε-水酸化亜鉛
| Material name | ε-Zinc hydroxide | |||||
| Composition | ε-Zn(OH)2 | |||||
| Chemical formula weight | 99.40 | |||||
| System | Orthorhombic | |||||
| Temperature (ºC) | r.t. | |||||
| a (Å), b (Å), c (Å) | 4.905(3) | 5.143(4) | 8.473(2) | |||
| α (deg), β (deg), γ (deg) | 90 | 90 | 90 | |||
| Unit cell volume (Å3) | 213.7 | |||||
| Calculated density (g/㎝3) | 3.09 | |||||
| Z | 4 | |||||
| Space group | P 212121 (No.19) | |||||
| atom | site | g | x/a | y/b | z/c | B (Å2) |
| Zn | 4a | 1 | 0.07096(6) | 0.64832(6) | 0.62420(4) | 1.009(3) |
| O1 | 4a | 1 | 0.1154(4) | 0.1256(4) | 0.0795(2) | 1.17(3) |
| O2 | 4a | 1 | 0.1670(4) | 0.3172(4) | 0.7198(2) | 1.18(3) |
| H1 | 4a | 1 | 0.501(9) | 0.36(1) | 0.857(6) | 1.0(7) |
| H2 | 4a | 1 | 0.28(1) | 0.79(1) | 0.170(6) | 1.0(7) |
| Comment | This ε-Zn(OH)2 is the most stable phase of five polymorphisms (α-, β-, γ-, δ-, and ε-phases). | |||||
Reference: R. Stahl, C. Jung, H.D. Lutz, W. Kockelmann, and H. Jacobs, Zeitschrift für Anorganische und Allgemeine Chemie, 624, 1130 (1998).