| Material name | Lanthanum lithium titanate | |||||
| Composition | La0.55Li0.35TiO3 | |||||
| Chemical formula weight | 174.69 | |||||
| System | Orthorhombic | |||||
| Temperature (ºC) | r.t. | |||||
| a (Å), b (Å), c (Å) | 7.7383(2) | 7.7422(1) | 7.7364(3) | |||
| α (deg), β (deg), γ (deg) | 90 | 90 | 90 | |||
| Unit cell volume (Å3) | 463.5 | |||||
| Calculated density (g/㎝3) | 5.01 | |||||
| Z | 8 | |||||
| Space group | Cmmm (No.65) | |||||
| atom | site | g | x/a | y/b | z/c | B (Å2) |
| La1 | 4i | 0.654(7) | 0 | 0.2483(18) | 0 | 0.41(6) |
| La2 | 4j | 0.446(7) | 0 | 0.257(3) | 1/2 | 0.41(6) |
| Li1 | 2c | 0.054(25) | 1/2 | 1/2 | 0 | 6.1(21) |
| Li2 | 4j | 0.673(25) | 1/2 | 0.183(8) | 1/2 | 6.1(21) |
| Ti | 8o | 1 | 0.2468(27) | 0 | 0.2491(11) | 1.13(7) |
| O1 | 4g | 1 | 0.2855(14) | 0 | 0 | 1.78(23) |
| O2 | 4h | 1 | 0.2153(15) | 0 | 1/2 | 1.83(25) |
| O3 | 4k | 1 | 0 | 0 | 0.2154(16) | 2.0(3) |
| O4 | 4l | 1 | 0 | 1/2 | 0.2680(17) | 1.5(3) |
| O5 | 8m | 1 | 1/4 | 1/4 | 0.2420(16) | 2.25(12) |
Reference: Y. Inaguma, T. Katsumata, M. Itoh, Y. Morii, and T. Tsurui, Solid State Ionics, 177, 3037 (2006).