結晶系
ギブサイト（ギブス石）（γ-水酸化アルミニウム）
| Material name | γ-Aluminum hydroxide (Gibbsite) | |||||
| Composition | γ-Al(OH)3 | |||||
| Chemical formula weight | 78.00 | |||||
| System | Monoclinic | |||||
| Temperature (ºC) | r.t. | |||||
| a (Å), b (Å), c (Å) | 8.675(1) | 5.0690(7) | 9.726(1) | |||
| α (deg), β (deg), γ (deg) | 90 | 94.55(1) | 90 | |||
| Unit cell volume (Å3) | 426.4(1) | |||||
| Calculated density (g/㎝3) | 2.43 | |||||
| Z | 8 | |||||
| Space group | P 1 21/n 1 (No.14) | |||||
| atom | site | g | x/a | y/b | z/c | B (Å2) |
| Al1 | 4e | 1 | 0.16788(5) | 0.52910(9) | -0.00220(5) | 0.55 |
| Al2 | 4e | 1 | 0.33442(5) | 0.02359(9) | -0.00236(5) | 0.56 |
| O1 | 4e | 1 | 0.1781(1) | 0.2182(2) | -0.1116(1) | 0.73 |
| O2 | 4e | 1 | 0.6695(1) | 0.6560(2) | -0.1027(1) | 0.68 |
| O3 | 4e | 1 | 0.4984(1) | 0.1304(2) | -0.1045(1) | 0.74 |
| O4 | 4e | 1 | -0.0204(1) | 0.6291(2) | -0.1071(1) | 0.67 |
| O5 | 4e | 1 | 0.2970(1) | 0.7175(2) | -0.1058(1) | 0.76 |
| O6 | 4e | 1 | 0.8192(1) | 0.1488(2) | -0.1019(1) | 0.71 |
| H1 | 4e | 1 | 0.098(3) | 0.153(6) | -0.127(3) | 2.76 |
| H2 | 4e | 1 | 0.595(3) | 0.570(6) | -0.103(3) | 3.24 |
| H3 | 4e | 1 | 0.498(3) | 0.107(5) | -0.192(2) | 2.05 |
| H4 | 4e | 1 | -0.056(3) | 0.778(6) | -0.117(3) | 4.74 |
| H5 | 4e | 1 | 0.294(3) | 0.718(6) | -0.188(2) | 2.37 |
| H6 | 4e | 1 | 0.807(2) | 0.152(5) | -0.189(2) | 1.26 |
| Comment | B values were calculated on the basis of U values in the reference. | |||||
Reference: K. Komatsu, T. Kuribayashi, Y. Kudoh, and H. Kagi, Zeitschrift für Kristallographie, 222(1), 1 (2007).