結晶系
α-三酸化二マンガン、α-酸化マンガン（III）
| Material name | α-Manganese (III) Oxide | |||||
| Composition | α-Mn2O3 | |||||
| Chemical formula weight | 157.88 | |||||
| System | Orthorhombic | |||||
| Temperature (ºC) | r.t. | |||||
| a (Å), b (Å), c (Å) | 9.4157(3) | 9.4233(3) | 9.4047(3) | |||
| α (deg), β (deg), γ (deg) | 90 | 90 | 90 | |||
| Unit cell volume (Å3) | 834.45 | |||||
| Calculated density (g/㎝3) | 5.03 | |||||
| Z | 16 | |||||
| Space group | Pcab (No.61) | |||||
| atom | site | g | x/a | y/b | z/c | B (Å2) |
| Mn1 | 4a | 1 | 0 | 0 | 0 | 0.34 |
| Mn2 | 4b | 1 | 0 | 0 | 1/2 | 0.42 |
| Mn3 | 8c | 1 | 0.28479(10) | 0.25253(5) | -0.00590(5) | 0.59 |
| Mn4 | 8c | 1 | 0.00462(5) | 0.28507(10) | 0.24564(5) | 0.59 |
| Mn5 | 8c | 1 | 0.25301(5) | 0.00130(4) | 0.28533(10) | 0.60 |
| O1 | 8c | 1 | 0.13299(32) | -0.08466(35) | 0.15030(33) | 0.66 |
| O2 | 8c | 1 | 0.14435(33) | 0.12989(34) | -0.08507(35) | 0.70 |
| O3 | 8c | 1 | -0.08038(35) | 0.14693(33) | 0.12412(31) | 0.62 |
| O4 | 8c | 1 | -0.37447(31) | 0.41757(34) | -0.35569(31) | 0.58 |
| O5 | 8c | 1 | -0.35081(32) | -0.37238(33) | 0.41947(35) | 0.65 |
| O6 | 8c | 1 | 0.41306(34) | -0.35285(33) | -0.36751(33) | 0.62 |
| Comment | B values were calculated on the basis of βij values in the reference. | |||||
Reference: S. Geller, Acta Crystallographica B, 27, 821 (1971).